ANALISA PENGARUH FRAKSI VOLUME SERAT PELEPAH AGEL PADA KOMPOSIT MATRIK EPOKSI TERHADAP KEKUATAN TARIK DAN BENDING YANG DIBUAT MENGGUNAKAN METODE VACCUM BAG

Pencarian berdasarkan :

SEMUA Pengarang Subjek ISBN/ISSN Pencarian Spesifik

Pencarian terakhir:

Tugas Akhir Mesin

ANALISA PENGARUH FRAKSI VOLUME SERAT PELEPAH AGEL PADA KOMPOSIT MATRIK EPOKSI TERHADAP KEKUATAN TARIK DAN BENDING YANG DIBUAT MENGGUNAKAN METODE VACCUM BAG

Safi’i Rahman - Nama Orang;

eed for components that have structural capabilities, light and strong, environmentally friendly materials are also the demands of today's technology. One material that is expected to be able to fulfill this is composite material with natural fiber filling material. The advantages of natural fibers are low density, easy to obtain, cheaper prices, environmentally friendly, and not harmful to health. In this study the natural fibers used are agel midrib fiber (corypha utan), as a filler and epoxy resin as a binder. The purpose of this study was to determine the effect of the volume fraction of agel midrib fibers on epoxy-based composites on tensile strength and bending strength which were made using the method vacuum bag. The fiber volume fraction used was 20%, 25%, and 30%. Based on the results of research conducted on the effect of the volume fraction of agel midrib fibers on epoxy chemistry composites showed that, variations in fiber volume fraction affect the tensile strength and bending strength of composites, where the highest average tensile strength was obtained in composites with 30% fiber volume fraction of 28, 13 N/mm2 and the lowest tensile strength at 20% fiber volume fraction of 16.45 N/mm2. While the highest average bending strength is obtained in composites with 30% fiber volume fraction of 39,40 N/mm2 and exposed to 20% volume fraction of 7,21 N/mm2. Judging from the results of SEM observations showed that thebond interface between fiber and epoxy is getting stronger with increasing fiber, the fiber full out is shorter so the tensile strength of the composite becomes high.

Ketersediaan

Tidak ada salinan data

Informasi Detail

Judul Seri: -
No. Panggil: 669.72.Saf.a
Penerbit: UNRAM : Fakultas Teknik Unram., 2018
Deskripsi Fisik: -
Bahasa: Indonesia
ISBN/ISSN: -
Klasifikasi: 669.72
Tipe Isi: other
Tipe Media: other
Tipe Pembawa: -
Edisi: Edisi 1 Jilid 1
Subjek: KOMPOSIT MATRIK
fiber volume fraction
ensile strength
strength bending and SEM observation
Info Detail Spesifik: -
Pernyataan Tanggungjawab: Safi’i Rahman

Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas

ANALISA PENGARUH FRAKSI VOLUME SERAT PELEPAH AGEL PADA KOMPOSIT MATRIK EPOKSI TERHADAP KEKUATAN TARIK DAN BENDING YANG DIBUAT MENGGUNAKAN METODE VACCUM BAG

Komentar

Anda harus login sebelum memberikan komentar