EFEK PERENDAMAN NaOH DAN KOH TERHADAP SIFAT KEKUATAN TARIK DAN MORFOLOGI DARI KOMPOSIT BERPENGUAT SERBUK KULIT WARU (HIBISCUS TILIACEUST)

Pencarian berdasarkan :

SEMUA Pengarang Subjek ISBN/ISSN Pencarian Spesifik

Pencarian terakhir:

Tugas Akhir Mesin

EFEK PERENDAMAN NaOH DAN KOH TERHADAP SIFAT KEKUATAN TARIK DAN MORFOLOGI DARI KOMPOSIT BERPENGUAT SERBUK KULIT WARU (HIBISCUS TILIACEUST)

Muhammad Rama Setiyadi - Nama Orang;

Composites made of fiber (fibrous composie) continue to be researched and developed to become an alternative material to replace metal materials, this is due to the nature of the fiber composite which is strong and has a lighter weight than metal. Composite composition consists of fiber or filler and matrix as the binding material. The aim of this study was to compare the tensile strength of composites reinforced with waru leather powder with alkaline NaOH and KOH treatment. The material used was waru leather powder with a polyester resin matrix, with a powder volume fraction of 5%, 10% and 20% with an alkaline treatment of 5% NaOH and 5% KOH with immersion for 2 hours, 4 hours, 6 hours and 8 hours. Tensile testing specimens and procedures refer to ASTM D3039 standard. The results of this study indicate the highest tensile strength with alkaline 5% NaOH treatment at 8 hours immersion with a 5% volume fraction of 33.33 MPa and the lowest tensile strength of 5% NaOH alkaline treatment at 2 hours immersion with 10% volume fraction of 22.97 MPa. While the highest tensile strength was 5% KOH alkaline treatment at 8 hours immersion with 10% volume fraction of 34.96 MPa and the lowest tensile strength was 5% KOH alkaline treatment at 6 hours immersion with 20% volume fraction of 21.96 MPa.

Ketersediaan

Tidak ada salinan data

Informasi Detail

Judul Seri: -
No. Panggil: 616. 342 7.Muh.e
Penerbit: Universitas Mataram : Fakultas Teknik Unram., 2021
Deskripsi Fisik: -
Bahasa: Indonesia
ISBN/ISSN: -
Klasifikasi: 616. 342 7
Tipe Isi: other
Tipe Media: computer
Tipe Pembawa: audio disc
Edisi: Edisi 1
Subjek: -
Info Detail Spesifik: EFEK PERENDAMAN NaOH DAN KOH TERHADAP SIFAT KEKUATAN TARIK DAN MORFOLOGI DARI KOMPOSIT
Pernyataan Tanggungjawab: Muhammad Rama Setiyadi

Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas

EFEK PERENDAMAN NaOH DAN KOH TERHADAP SIFAT KEKUATAN TARIK DAN MORFOLOGI DARI KOMPOSIT BERPENGUAT SERBUK KULIT WARU (HIBISCUS TILIACEUST)

Komentar

Anda harus login sebelum memberikan komentar